Features

• Pressure-Sensitive Adhesion
  Curing reaction is caused by moisture absorbed from the air. Pressure-sensitive range is reached in this curing process about 10 min. after application. If adherends are put together during this time, they bound instantaneously as in the case of rubber contact adhesive, eliminating the need for temporary fixation.
• One-part solventless agent providing quick curing at normal temperature
  Easy-to-use, safe, and clean cemedine adhesive featuring one-part solventless agent capable of quick curing at normal temperature is provided.
• Adhesive property over an Extensive Range
  Cemedine Super-X 8008 products allow for adhesion of various types of plastics, rubbers and ceramics over an extensive range, moreover different types of metals. These products provides excellent adhesion over a very extensive range of materials, eliminating the need for selecting a particular adhesive for each type of the different materials, as in the case of conventional agents.
• Durability
  The Super-X as elastic adhesives do not peel off. Once materials are adhered, the Cemedine Super-X provides durability in the range from low temperature (-60°C) to high temperature (120°C). Because of the rubber state of the hard film, the Super-X follows the changes of adherents such as expansion and shrinkage sufficiently.

Applications

• Adhesion required to have initial adhesive strength
• Adhesion of different types of materials having different thermal expansion coefficients
• Electrical contact failure countermeasure product

Adhesive strength for various types of adherends

Conditions: Coated on both sides, 50µm thick (one side), tension speed between adherends: 50mm/min.

Note:

*1 and *2: Surface preparation will cause adhesive strength to become uneven; it must be confirmed in advance.
*3: Primer (Cemedine PP-7F) to be used.

Adhesive strength for various types of rubbers

(*): Degreasing by toluene after treatment by sand paper (#120).